| PHYSICAL PROPERTIES |
| PRODUCT | ; ADHESION PROMOTED POLYESTER FILM |
| TYPE (CODE) | ; FCMO (FOR SOLVENT BASED) |
| MAIN USAGE | ; PRINTING, COATING & METALLIZING |
| PROPERTIES | UNIT | TYPICAL VALUES | TEST METHOD | |||||
| Average Thickness | § | 12 | 23 | 25 | - | |||
| Tensile Strength | MD | §¸/§± psi¡¿10©ø |
27 38 |
35 36 |
25 36 |
ASTM D-882 | ||
| TD | §¸/§± psi¡¿10©ø |
26 37 |
24 34 |
24 34 |
||||
| Elongation at break |
MD | % | 134 | 136 | 138 | ASTM D-882 | ||
| TD | % | 135 | 136 | 139 | ||||
| F-5 Value | MD | §¸/§± psi¡¿10©ø |
12 17 |
12 17 |
12 17 |
ASTM D-882 | ||
| TD | §¸/§± psi¡¿10©ø |
11 16 |
11 16 |
11 16 |
||||
| Heat
Shrinkage (in hot air) |
MD | % | 1.2 | 1.0 | 1.0 | ASTM
D-2305 (150¡É, 30 min) |
||
| TD | % | 0.0 | 0.0 | 0.0 | ||||
| Friction Coefficient (film/film ; in/out) |
¥ìs | - | 0.28 | 0.27 | 0.26 | ASTM D-1894 | ||
| ¥ìk | - | 0.36 | 0.30 | 0.26 | ||||
|
Wetting Tension (coated ; in) |
In | dynes/cm | 40 | 40 | 40 | ASTM D-2578 | ||
| Out | dynes/cm | 40 | 40 | 40 | ||||
| Haze | % | 2.7 | 3.1 | 3.4 | ASTM D-1003 | |||
| Test Condition | ¡¤Normal laboratory ambient condition ; 23¡É, 50% RH | |||||||